Stainless Steel Patti ASTM A182

Price 250 INR/ Kilograms

Get a Price/Quote

Stainless Steel Patti ASTM A182 Specification

Diameter
N/A (Flat strip)

Size
Varies (customizable per order)

Product Form
Flat strip/patti

Heat Resistance
Yes

Coating Type
Uncoated

Corrosion Resistant
Yes

Tensile Strength
Min. 515 MPa

Material Composition %
Cr: 18-20%, Ni: 8-12%, C: 0.08%

Hardness
Max 200 HB

Recyclable
Yes

Product Name
Stainless Steel Patti ASTM A182

Steel Type
Stainless Steel

Steel Product Type
Patti / Strip

Grade
ASTM A182

Thickness
0.18-2.5 Millimeter (mm)

Shape
Flat

Steel Standard
ASTM A182

Surface
Smooth, Mill finish

Composition
Alloy steel, primarily Chromium and Nickel based

Application
Industrial, Construction, Manufacturing, Fabrication

Dimension (L*W*H)
Customizable, typically supplied in lengths up to 6 meters, width as per requirement

Weight
Varies based on dimensions, approx. 1.44 kg/m for 0.18mm thickness

Color
Grey

Material Grade
ASTM A182

Finish Type
Mill finish, also available in brushed or polished

Usage
Used for support, reinforcement, edge protection, and framing

Elongation
Min. 30%

Weldability
Excellent

Delivery Condition
Hot rolled/Cold drawn

MOQ
100 kg

Magnetic Properties
Non-magnetic

Machinability
Good

Density
7.8 g/cm³

Edge Type
Straight cut, optionally deburred

Packing Type
Bundle or coil, wrapped for protection

About Stainless Steel Patti ASTM A182

Product details

Elongation	35%
Features	Corrosion resistant,Accurate dimensions,Can sustain high pressure &amp; temperature load,Rust proof
Application	Automobile Industry,Oil &amp; Gas Industry,Pharmaceutical / Chemical Industry,Construction
Usage/Application	Automobile Industry
Material Standard	ASTM A182
Thicknesses	0.18 mm to 2.5 mm
Brand	Nascent
Tensile Strength	1450 Mpa
Standard	ASTM A182
Color	Grey
Material	Stainless Steel

Determinations:

Thickness: 0.18 mm to 2.5 mm
Width: max. 1800 mm

Superior Material Quality and Versatility

This ASTM A182 stainless steel patti is crafted from a premium chromium-nickel alloy, ensuring robust mechanical properties, including a minimum tensile strength of 515 MPa and elongation of at least 30%. Its versatile, flat strip form accommodates a range of industrial and structural applications, serving as reinforcement, edge protection, or framing in diverse projects. Supported by precise manufacturing processes, each piece offers exceptional consistency and durability.

Optimal Performance for Demanding Environments

Designed to withstand corrosion, heat, and demanding operating conditions, the patti is suitable for use up to 870C. Its non-magnetic nature makes it ideal for sensitive environments and electrical applications. The mill finish surface guarantees smoothness, and custom dimensions cater to specific project needs, making it a reliable component whether you are an importer, exporter, distributor, or manufacturer.

FAQ's of Stainless Steel Patti ASTM A182:

Q: How is Stainless Steel Patti ASTM A182 typically used in industrial applications?

A: This patti is primarily used for support, reinforcement, framing, and edge protection in construction, manufacturing, and fabrication settings. Its robust quality makes it suitable for demands where corrosion and heat resistance are essential.

Q: What processes are available for manufacturing this stainless steel patti?

A: The patti is produced through hot rolling or cold drawing processes, ensuring precision and surface finish. Clients can choose between smooth mill finish, brushed, or polished finishes to suit their application requirements.

Q: When can I expect delivery after placing an order, and what is the minimum order quantity (MOQ)?

A: Typical lead times depend on the order size and specifications, but deliveries are expedited as much as possible. The minimum order quantity is 100 kilograms, making it suitable for both small and large-scale projects.

Q: Where is Stainless Steel Patti ASTM A182 commonly supplied in India?

A: We cater to buyers across India, including dealers, distributors, fabricators, manufacturers, producers, retailers, and wholesalers, supporting a wide range of industrial sectors.

Q: What are the benefits of using ASTM A182 Grade stainless steel for patti applications?

A: Benefits include high tensile strength (min. 515 MPa), excellent corrosion and heat resistance, non-magnetic properties, good machinability, and overall durability. Its recyclable nature also underlines environmental responsibility.