Stainless Steel Round Bar 316 L

Price 250 INR/ Kilograms

Get a Price/Quote

Stainless Steel Round Bar 316 L Specification

Recyclable
Yes

Diameter
6 mm to 200 mm or as specified

Heat Resistance
Yes

Tensile Strength
515 - 690 MPa

Material Composition %
Chromium 16-18%, Nickel 10-14%, Molybdenum 2-3%, Carbon 0.03%

Size
Custom sizes available; diameter & length as required

Coating Type
None; natural finish

Product Form
Solid, Round Bar

Corrosion Resistant
Excellent; high resistance to pitting and crevice corrosion

Hardness
217 HB

Product Name
Stainless Steel Round Bar 316 L

Steel Type
Austenitic Stainless Steel

Steel Product Type
Round Bar

Grade
316L

Thickness
N/A (round bar; refer to diameter)

Shape
Round

Steel Standard
ASTM A276 / A479, EN 10088-3

Surface
Bright, Smooth

Composition
Cr: 16-18%, Ni: 10-14%, Mo: 2-3%, C: 0.03%, Mn: 2%, Si: 1%

Application
Industrial fabrication, construction, marine, chemical processing, food industry, pharmaceuticals

Dimension (L*W*H)
Custom lengths, round cross-section, varies per requirement

Weight
Varies based on diameter and length

Color
Silver

Material Grade
316L

Finish Type
Bright/Polished

Usage
Machining, shafts, valves, fasteners, marine fixtures, medical equipment

Weldability
Excellent; suitable for all standard welding techniques

Modulus of Elasticity
193 GPa

Machinability
Good (better with chip breakers and rigid tools)

Magnetism
Non-magnetic in annealed condition

Density
7.98 g/cm

Melting Point
1400 1450C

Yield Strength
205 MPa min

Elongation
40% min (in 50mm)

Lead Time
Depends on quantity and size; typically 3-7 business days

About Stainless Steel Round Bar 316 L

Stainless Steel Round Bar 316 L Specifications

Form	Round, Square, Hex A/F,Rectangle, Billet, Ingot, Forging Etc.
Usage/Application	Construction
Standard	ASTM A276,ASME SA276 / ASTM A479 ASME SA479
Brand	Nascent
Packaging Type	Standard
Color	Silver
Size	As Per Customer Requirement
Material	Stainless Steel
Application	Paper & Pulp Companies, High Pressure Applications, Oil and Gas Industry, Chemical Refinery, Pipeline

Superior Corrosion Resistance

Stainless Steel Round Bar 316L offers outstanding resistance to pitting and crevice corrosion due to its high molybdenum and chromium content. This makes it ideal for harsh, saline, or chemical-rich environments, ensuring durability and longevity in critical applications such as marine equipment, chemical plants, and food processing lines.

Customizable for Your Needs

Available in diameters ranging from 6mm to 200mm and in lengths tailored to your specifications, 316L round bars can be sourced to perfectly match your project requirements. With a polished, bright finish and strict adherence to ASTM and EN standards, they deliver both form and function, making them a top choice for fabricators and engineers.

Effortless Fabrication and Welding

316L stainless round bars are renowned for their excellent weldability, easily accommodating all standard welding techniques without the need for pre- or post-heat treatments. Their good machinability is further enhanced by using chip breakers and rigid tools, ensuring precise and efficient fabrication across various industries.

FAQ's of Stainless Steel Round Bar 316 L:

Q: How can I use Stainless Steel Round Bar 316L in marine or chemical environments?

A: 316L round bars are specifically engineered for high resistance to pitting and crevice corrosion, making them exceptionally suited for marine, chemical, and food industry settings where frequent exposure to harsh solutions or saline water occurs.

Q: What are the benefits of choosing 316L stainless steel over other grades?

A: 316L offers superior corrosion resistance, especially against chlorides and industrial chemicals, due to its low carbon and higher molybdenum content. It maintains strength at elevated temperatures and ensures excellent ductility (elongation min 40%) and weldability.

Q: When should I specify a customized diameter or length for this product?

A: Custom diameters (6mm-200mm) and lengths can be ordered to suit your particular project or application needs. This flexibility reduces material waste and ensures compatibility with your design specifications. Lead times generally range from 3-7 business days depending on your requirements.

Q: Where can Stainless Steel Round Bar 316L be applied?

A: Typical applications include industrial fabrication, construction, marine fixtures, food industry equipment, chemical processing, pharmaceuticals, shafts, valves, fasteners, and even medical devices. Its versatility and robustness make it suitable across many sectors.

Q: What is the process for ordering and fabricating 316L round bars?

A: Place your order specifying the required diameter and length. The bars will be produced per ASTM A276/A479 or EN 10088-3 standards. Fabrication is straightforward thanks to their excellent weldability and good machinability, especially with the right tools.

Q: How does the non-magnetic property of 316L round bars benefit certain applications?

A: In the annealed condition, 316L is non-magnetic, an advantage in sensitive instrumentation, food processing, and medical environments where magnetic interference must be minimized.